SANDSTROM LC-300 涂层

点击图片查看原图
品 牌: 比尔安达 
型 号: SANDSTROM LC-300 涂层 
规 格: 10*50 
单 价: 1.00元/件 
起 订: 1 件 
供货总量: 111213 件
发货期限: 自买家付款之日起 3 天内发货
所在地: 上海
有效期至: 长期有效
最后更新: 2021-10-13
浏览次数: 2398
询价
公司基本资料信息
 
 
产品详细说明
 SANDSTROM LC-300 CONTAINS NO LEAD OR GRAPHITE
TYPICAL USES
Sandstrom LC-300 is an excellent solution to the problem of
lubricating parts:
• Where "clean operation" is desired (LC-300 will not collect dirt and
debris as do grease and oils)
• Where parts may be subjected to frequent disassembly
• Where a protective coating and sacrificial break-in lubricant are
needed
• Where fretting and galling is a problem (such as splines, universal
joints, and keyed bearings)
• Where easy release is desired (such as acme nuts and screws
and PVC molds)
• Where metallurgical properties are adversely affected by baking
at temperatures higher than 300 o F
• That will be operated in corrosive atmospheres
• That may be stored for long periods
• Which are seldom lubricated once they leave the factory and
where permanent lubrication is desired
• Where operating pressures exceed the load-bearing capacities of
ordinary oils and greases
COMPOSITION AND PHYSICAL PROPERTIES
Net Weight per gallon 10.20 lbs + .2 lb
Solids content 41.0% + 1%(By Wt.)
Viscosity 80-95 sec / #1 Zahn
Flash point 43 o F + 2 o F Setaflash
Operating temperature
range -320 o F to +400 o F
Wear life 298 minutes average
ASTM D2625A
Load carrying capacity 2750 lbs. *
ASTM D2625B
Vehicle type Modified Vinyl
Lubricative pigment Molybdenum Disulfide
Color Flat Dark Gray
Shelf life 1 year from date of manufacture
Specifications SAE Spec AS5272C Type I
PRI QPL AS5272 type 1
Corrosion protection
Sulfurous Acid-Salt Spray 4 cycles with no effect *
Fed-STD-791c Method 5331.1
ASTM B117 1000 hours*
MIL-DTL-16232 type M or Z class3
TECHNICAL INFORMATION GUIDE
PORT BYRON, IL 61275 • (309) 523-2121
1-800-747-1084 FAX # 1-309-523-3912
*Tests halted before failure
GENERAL
Sandstrom LC-300 is a paint-like material consisting of lubricative
pigments dispersed in a thermosetting resin system thinned with appropri-
ate solvents. For maximum service, the APPLICATION INSTRUCTIONS
MUST BE FOLLOWED CLOSELY. The lubricant is flammable and the safety
precautions usually followed when using flammable materials should be
observed.
FILM THICKNESS AND ENGINEERING TOLERANCES
As supplied, Sandstrom LC-300 will yield a film thickness of about .0005
inches per dip coat. Usually engineering tolerances will permit necessary
minimum film buildup of .0002 to .0003 inches without interference. If
excess buildup does occur and a force fit is necessary, burnishing lightly
will assist in mating the parts. The remaining excess will be worn away in
the first few cycles of operation. Whenever possible, the proper tolerances
should be designed into the part.
COVERAGE
One gallon of this material will cover 625 sq. ft. with a dry film thickness
of .0005 inches. Coverage depends upon methods of application and other
variables such as overspray and type of surface to be coated. Above
coverage rates are based on 100% efficiency.
SURFACE PREPARATION
The following surface preparations are recommended for the individual metals
listed in the Application Appendix of the military specification to develop
maximum adhesion, wear life, and corrosion protection. Please contact
Sandstrom Products Company for substitute surface preparations if recom-
mended steps cannot be followed.
Application on steel. Preclean the steel surface with aliphatic naphtha or
any other EPA compliant cleaner that sufficiently cleans surfaces to pass
ASTM F22. Sandblast the surfaces with 180-220 grit aluminum oxide. Phos-
phate IAW MIL-DTL-16232 (weight should be 11-22 g/m 2 ), type M, class 3 or
type Z, class 3.
Application on stainless steels. Preclean the steel surface with
aliphatic naphtha or any other EPA compliant cleaner that sufficiently
cleans surfaces to pass ASTM F22. Sandblast the surfaces with 120 grit
aluminum oxide. Passivate the surfaces with ASTM A967, types nitric 1,
nitric 2 or nitric 3, as applicable.
Application on aluminum and aluminum alloys. Preclean the
aluminum surface with aliphatic naphtha or any other EPA compliant
cleaner that sufficiently cleans surfaces to pass ASTM F22. Sulfuric acid
anodize IAW MIL-A-8625 and seal the surface.
Application on titanium and titanium alloys. Degrease the surfaces
to be coated with aliphatic naphtha or any other EPA compliant cleaner that
sufficiently cleans surfaces to pass ASTM F22. Sandblast the surface
with 180-220 grit aluminum oxide and alkaline anodize.
Application on copper and copper alloys. Preclean the copper
surface with aliphatic naphtha or any other EPA compliant cleaner that
sufficiently cleans surfaces to pass ASTM F22. Sandblast the surfaces
with 180-220 grit aluminum oxide. Form a black oxide finish on the
surfaces.
importANT! DO NOT TOUCH CLEAN SURFACE WITH
FINGERS - OIL FROM THE HANDS WILL INTERFERE WITH
PROPER COATING ADHESION. Whenever possible, treat both
contact surfaces (i.e., the shaft and the bearing).
Page 2; Series V765, LC-300 Solid Film Lubricant-Heat Curing
NOTICE
Before using this product, read all warnings and safety infor-
mation printed on the label, the Material Safety Data Sheet, and
the Technical Information Guide.
STIRRING
importANT! THIS LUBRICANT CONTAINS HEAVY PIGMENTS
WHICH SETTLE RAPIDLY. THEREFORE, IT SHOULD BE
STIRRED THOROUGHLY BEFORE USE AND CONTINUOUSLY
DURING APPLICATION.
THINNING
For spraying - Sandstrom LC-300 may be thinned using D169
Thinner. The suggested starting point is 2 parts LC-300 to 1
part thinner.
For dipping - IF NECESSARY, use a slow drying thinner such
as PM acetate in such proportions as to provide proper runoff
characteristics. The suggested starting point is 4 parts of LC-
300 to 1 part thinner.
APPLICATION
Sandstrom LC-300 should be sprayed or dipped to the de-
sired film thickness (usually .0003 to .0007 inches). Allow the
surface to dry at least 30 minutes at 77 o F + 5 o F and at less than
70% relative humidity before baking. Lower temperatures and/
or higher humidity may require longer dry time to prevent
defects.
BAKING
BAKING AT 300 o F FOR ONE (1) HOUR in a forced draft oven
WILL YIELD OPTIMUM CORROSION PROTECTION AND
WEAR LIFE.
importANT! The hour begins when the part has reached
300 o F NOT when it is placed in the oven. In cases of very thick
metals, an extra hour may be required to bring the part up to
the proper temperature. Thermocouples may be used to
determine the true temperature of the metal.
To test for complete cure, light rubbing with MEK on a rag will
not remove coating to bare metal.
CLEANUP
Use the same solvents for cleaning tools as are recom-
mended for thinning.
REMOVAL OF SANDSTROM LC-300
In the event it is necessary to remove Sandstrom LC-300,
physical removal is best (such as grit blasting, sanding, or
grinding). Also, selected epoxy cold strippers will remove LC-
300.
*Strict compliance to the instructions given in Surface Prepa-
ration, Thinning, Application, and Baking is very essential for
obtaining optimum results.
WARNINGS: Constant stirring is imperative for best results.